Properties 

Polyphthalamide
/Extra-tough

Topics   Index

**************************************
Copyright 2002 by Roger D. Corneliussen
**************************************

Values are from Modern Plastics Encyclopedia 99.

To jump to a particular property, click on the name listed below.

Melt Flow
Melting Temperature
Glass Transition
Processing Molding Pressure
Processing Molding Temperature
Compression Ratio
Mold Shrinkage
Tensile Strength
Elongation
Tensile Yield Strength
Compressive Strength
Flexural Strength
Tensile Modulus
Flexural Modulus
Izod Impact Strength
Hardness
Deflection Temperature
Thermal Expansion
Thermal Conductivity
Specific Gravity
Dielectric Strength
Water Absorption

Note: The ASTM numbers are linked to 
their descriptions on the ASTM website.  
To go to the description, simply
click on the ASTM number

Melt Flow 
ASTM D1238
(gm/10 min)

--- gm /10 min

Melting Temperature  degrees C
Tm Crystalline
310 C

Glass Transition (C)
Tg (Amorphous)

--- C

Processing Temperature Range Degrees F
Extrusion

610 to 675 F; Injection Molding

Molding Pressure Range ( PSI) (ksi)
5000 to 15000 psi
5 to 15 ksi
33 to 100 MPa

To go back to the top of this page, click on
Top

Compression Ratio
2.5 to 3

Mold(Linear) Shrinkage (in/in)
ASTM D955
0.015 to 0.020 in/in 

Tensile Strength at Break
ASTM D638
11000 psi
73 MPa

To go back to the top of this page, click on
Top

Elongation at break (%)
ASTM D638
30 %

Tensile Yield Strength (psi)
ASTM D638
10500 psi
70 MPa

Compressive Strength (psi)
Rupture or Yield
ASTM D695
--- psi
--- MPa

To go to Compressive Strength Values,
click on
Compressive Strength

To go back to the top of this page, click on
Top

Flexural Strength (psi)
Rupture or Yield
ASTM D790
17000  psi
113 MPa

Tensile Modulus (psi)
ASTM D638
350000 psi
2.3 GPa

To go to Modulus Values,
click on
Modulus

Compressive Modulus (psi)
ASTM D695
--- psi
--- GPa

To go back to the top of this page, click on
Top

Flexural Modulus (psi)
ASTM D790
At 73 F
368000 psi
2.5 GPa
At 200 F
--- psi
--- GPa
At 250 F
--- psi
--- GPa
At 300 F
--- psi
--- GPa

Izod Impact (ft-lb/in of notch)
ASTM D256

18  ft lb/in of notch

To go to Izod Values,
click on
Izod

To go back to the top of this page, click on
Top

Hardness
Rockwell ASTM D785
120
--
Shore D65 ASTM D2240/D2583
---

Coefficient of Linear Thermal Expansion
(10 exp-6 )in/in/C
--- (10 x exp 6) in/in /C
---  in/in /C

Deflection Temperature under flexural load (F)
ASTM D648
264 psi ---
243 F
66 psi  ---
--- F

To go back to the top of this page, click on
Top

Thermal Conductivity
(10 x exp 4)al cm/sec cm2 C
ASTM C177
--- (10 x exp 4) cal cm/sec cm2
--- cal cm/sec cm2

Specific Gravity
ASTM D792
1.15

To go to Density /Specific Gravity Values,
click on
Density

Water Absorption
(1/8 in thick specimen) (%)
ASTM D570
24 hr --- 0.68 %
Saturation 
---  %

Dielectric Strength v/mil
(1/8 in thick Specimen; short time)
--- v/mil

**************************************

To go back to the top of this page, click on
Top

Topics   Index

**************************************
Copyright 2002 by Roger D. Corneliussen
No part of this transmission is to be
duplicated, in any manor, or forwarded by
electronic mail without the express written
permission of Roger D. Corneliussen
**************************************

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Number of visits since 4/18/2000:
Hit Counter